Hubei Kepuda Polymer Material Co., Ltd.
Polyethylene Compound
Category:
The product was prepared by twin screw extrusion of new polyethylene, it has features of stable quality, excellent processing technique, wide processing temperature. It can replace imported products and be supplied timely.
Contact:
Product Center
-
Polyethylene Compound
-
Thermoplastic Low-Smoke Halogen-Free Flame-Retardant Polyolefin Cable Compound
-
Irradiation Crosslinkable Low-Smoke Halogen-Free Flame-retardant Polyolefin Cable Compound
-
Anti-Tracking Polyethylene Sheathing Compound for ADSS Optical Cable
-
Eco-Friendly Rodent-Proof and Termite-Proof Nylon Sheathing Compound
-
Flame-Retardant Polyethylene Compound
-
Elastomer Cable Compound
-
Special Cable Compounds and Solutions
Product Performance
The product was prepared by twin screw extrusion of new polyethylene; it has features of stable quality, excellent processing technique, wide processing temperature. It can replace imported products and be supplied timely.
Product Model
| Type | Product | Application |
| KPH0802-N | New Black HDPE compound |
Wire & Cable Jacket |
| KPM0801-N | New Black MDPE compound |
Wire & Cable Jacket |
| KPL0803-N | New Black LLDPE compound |
Wire & Cable Jacket |
Processing technology
The following temperature profile for the extruder is recommended:
|
Zone |
Zone1 |
Zone2 |
Zone3 |
Zone4 |
Zone5 |
Head |
Die |
|
|
Temperature ℃ |
HDPE | 160 | 190 | 220 | 235 | 235 | 235 | 235 |
| MDPE | 160 | 180 | 220 | 235 | 235 | 230 | 230 | |
| LLDPE | 140 | 160 | 200 | 220 | 220 | 210 | 210 | |
Storage and Transportation
Packaging: 750 kg, 500 kg polyethylene inner bag with outer woven bag; or 25 kg paper-plastic lamination bag.
Transportation: avoid sunshine, rainfall and moisture; keep the packaging intact.
Storage: Please store in a clean, cool, dry, and well-ventilated warehouse; keep away from sources of ignition. If the product becomes damp, please dry it at temperatures between 60-80°C for 1 to 2 hours.
Performance metrics
|
Property |
Unit |
Typical value | ||
| KPH0802-N | KPM0801-N | KPL0803-N | ||
|
Density |
g/cm3 | 0.960 | 0.945 | 0.938 |
|
Melting Index (190℃) |
g/10min | 0.5 | 0.7 | 1.3 |
|
Tensile Strength |
MPa | 30 | 28 | 23 |
|
Elongation at break |
% | 800 | 800 | 800 |
|
Brittle temperature (-76℃) |
- | PASS | PASS | PASS |
|
ESCR |
h | ≥1000 | ≥1000 | ≥1000 |
|
Carbon black content |
% | 2.6 ± 0.25 | 2.6 ± 0.25 | 2.6 ± 0.25 |
|
Dispersity of carbon black |
grade | 2.5 | 2.5 | 2.5 |
|
OIT200℃ |
min | 60 | 60 | 60 |
|
Dielectric strength |
MV/m | 30 | 26 | 30 |
|
Volume resistivity at 20℃ |
Ω·m | 2x1014 | 2x1014 | 3x1014 |
|
Dielectric constant |
- | 2.5 | 2.5 | 2.5 |
Keywords:
Polyethylene Compound
Production strength
Honorary Qualifications
Related products
Contact Information
Company office
Sales Hotline
Procurement Hotline
Company headquarters
No. 168, Yanjiang Road, Xiaochi Town, Huangmei County, Hubei Province
Follow us