Hubei Kepuda Polymer Material Co., Ltd.
Polyethylene Compound
Category:
KPH0802-HLS adopts imported polyethylene resin as raw material. It has features of high size stability, smooth surface, low shrinkage performance, processing and mechanical properties.
Contact:
Product Center
-
Polyethylene Compound
-
Thermoplastic Low-Smoke Halogen-Free Flame-Retardant Polyolefin Cable Compound
-
Irradiation Crosslinkable Low-Smoke Halogen-Free Flame-retardant Polyolefin Cable Compound
-
Anti-Tracking Polyethylene Sheathing Compound for ADSS Optical Cable
-
Eco-Friendly Rodent-Proof and Termite-Proof Nylon Sheathing Compound
-
Flame-Retardant Polyethylene Compound
-
Elastomer Cable Compound
-
Special Cable Compounds and Solutions
Product Performance
KPH0802-HLS adopts imported polyethylene resin as raw material. It has features of high size stability, smooth surface, low shrinkage performance, processing and mechanical properties.
Product Model
|
Type |
Product |
Application |
|
KPH0802-HLS |
Low-shrinkage high density polyethylene cable compound |
Used for manufacturing of air-blown micro cable |
Processing technology
The following temperature profile for the extruder is recommended:
|
Zone |
Zone1 |
Zone2 |
Zone3 |
Zone4 |
Zone5 |
Head |
Die |
|
Temperature |
200 |
220 |
230 |
240 |
245 |
240 |
240 |
Storage and Transportation
KPH0802-HLS is hygroscopic. It should be stored in dry and ventilated warehouse. And drying treatment is required after long-term storage. Drying temperature is 75℃. Drying time is 3 hours. Storage period should be less than 12 months.
Performance metrics
| No. |
Item |
Unit |
Typical |
Test method |
|
1 |
Melting Index |
g/10min |
0.27 |
GB/T 2951.41 |
|
2 |
Density |
g/cm³ |
0.951 |
GB/T 1033 |
|
3 |
Tensile Strength |
MPa |
33 |
GB/T 1040 |
|
4 |
Yield strength |
MPa |
20 |
GB/T 1040 |
|
5 |
Elongation at Break |
% |
810 |
GB/T 1040 |
|
6 |
Low temperature elongation at break |
% |
480 |
GB/T 2951.13 |
|
7 |
Brittle temperature （-76℃） |
pcs |
0/10 |
GB/T 5470 |
|
8 |
ESCR |
h |
> 1000 |
GB/T 2951.41 |
|
9 |
200℃ OIT |
min |
60 |
GB/T 2951.39 |
|
10 |
Dielectric Strength |
MV/m |
28 |
GB/T 1408 |
|
11 |
Volume Resistivity at 20℃ |
Ω·m |
4.5 × 1014 |
GB/T 1410 |
|
12 |
Dielectric constant |
— |
2.1 |
GB/T 1409 |
|
13 |
Dielectric loss tangent |
|
0.0003 |
GB/T 1409 |
|
14 |
Cabling shrinkage |
% |
0.04 |
- |
|
15 |
Surface roughness |
GB/T 1031-2009 |
||
|
|
Ra |
μm |
0.49 |
|
|
|
Ry |
μm |
3.2 |
|
Keywords:
Polyethylene Compound
Production strength
Honorary Qualifications
Related products
Contact Information
Company office
Sales Hotline
Procurement Hotline
Company headquarters
No. 168, Yanjiang Road, Xiaochi Town, Huangmei County, Hubei Province
Follow us