Hubei Kepuda Polymer Material Co., Ltd.
Thermoplastic Low-Smoke Halogen-Free Flame-Retardant Polyolefin Cable Compound
Thermoplastic low-smoke halogen-free flame-retardant polyolefin material has excellent mechanical property, flame-retardant property, anti-cracking property and low-temperature property with oxygen index ranging from 30 to 45 in various specifications.
Contact:
Product Center
-
Polyethylene Compound
-
Thermoplastic Low-Smoke Halogen-Free Flame-Retardant Polyolefin Cable Compound
-
Irradiation Crosslinkable Low-Smoke Halogen-Free Flame-retardant Polyolefin Cable Compound
-
Anti-Tracking Polyethylene Sheathing Compound for ADSS Optical Cable
-
Eco-Friendly Rodent-Proof and Termite-Proof Nylon Sheathing Compound
-
Flame-Retardant Polyethylene Compound
-
Elastomer Cable Compound
-
Special Cable Compounds and Solutions
Product Performance
Thermoplastic low-smoke halogen-free flame-retardant polyolefin material has excellent mechanical property, flame-retardant property, anti-cracking property and low-temperature property with oxygen index ranging from 30 to 45 in various specifications.
Product Model
|
Type |
Product |
Application |
|
KPW-5895 |
Thermoplastic low-smoke halogen-free flame-retardant polyolefin cable compound |
For indoor wire of high FR rating |
|
KPW-5895TKUV-1 |
Thermoplastic low-smoke halogen-free flame-retardant polyolefin cable compound |
For indoor wire of high FR rating |
Processing technology
The following temperature profile for the extruder is recommended:
|
Zone |
Zone1 |
Zone2 |
Zone3 |
Zone4 |
Zone5 |
Head |
Die |
|
|
Temperature ℃ |
KPW-5895 KPW-5895TKUV-1 |
130 |
140 |
150 |
160 |
165 |
165 |
165 |
Storage and Transportation
Product adopts moisture proof packaging; net weight is 25kg; be stored in clean, dry and ventilated place; drying treatment is required after long-term storage; drying temperature is 75℃; drying time is 3 hours; storage period should be less than 12 months.
Performance metrics
|
NO. |
Item |
Unit |
Typical |
Test method |
|||
|
KPW-5895 |
KPW-5895 TKUV-1 |
||||||
|
1 |
Density |
g/cm³ |
1.51 |
1.53 |
GB/T 1033 |
||
|
2 |
Tensile Strength |
MPa |
12 |
12.5 |
GB/T 1040 |
||
|
3 |
Elongation at Break |
% |
170 |
155 |
|
||
|
4 |
Thermal Aging Property |
℃ ×day |
110 × 240 |
110 × 240 |
GB/T 2951.7 |
||
|
4.1 |
Variation on Tensile Strength |
% |
13 |
-14 |
|
||
|
4.2 |
Variation on Elongation |
% |
-15 |
-15 |
|
||
|
5 |
Hot Deformation（90℃× 4h） |
% |
18 |
7 |
GB/T 2951.31 |
||
|
6 |
Brittle Temperature at -40℃ |
pcs |
0 |
0 |
GB/T 5470 |
||
|
7 |
Volume Resistivity at 20℃ |
Ω·m |
2.8 × 1012 |
1.2 × 1012 |
GB/T 1410 |
||
|
8 |
Dielectric Strength |
MV/m |
26 |
26 |
GB/T 1408 |
||
|
9 |
Smoke Density |
Flaming |
—— |
58 |
58 |
ASTM E 662 |
|
|
No flaming |
—— |
186 |
186 |
||||
|
10 |
Oxygen Index |
% |
36 |
38 |
GB/T 2406 |
||
|
11 |
Content of Halogen Acid |
IEC 60754-2 |
|||||
|
11.1 |
pH Value |
—— |
5.9 |
5.9 |
|||
|
11.2 |
Electrical Conductivity |
μS/mm |
1.2 |
1.2 |
|||
|
12 |
Toxicity Index |
—— |
1 |
1 |
NES 713 |
||
|
13 |
Hardness |
Shore D |
57 |
60 |
IEC 60811 |
||
Keywords:
Thermoplastic Low-Smoke Halogen-Free Flame-Retardant Polyolefin Cable Compound
Production strength
Honorary Qualifications
Related products
Contact Information
Company office
Sales Hotline
Procurement Hotline
Company headquarters
No. 168, Yanjiang Road, Xiaochi Town, Huangmei County, Hubei Province
Follow us