Hubei Kepuda Polymer Material Co., Ltd.
Special Cable Compounds and Solutions
Category:
KPG-0808 is an optical cable skeleton material developed through special formula by taking imported polyethylene resin as raw material. It has high size stability, smooth surface effect, low shrinkage performance and mechanical property.
Contact:
Product Center
-
Polyethylene Compound
-
Thermoplastic Low-Smoke Halogen-Free Flame-Retardant Polyolefin Cable Compound
-
Irradiation Crosslinkable Low-Smoke Halogen-Free Flame-retardant Polyolefin Cable Compound
-
Anti-Tracking Polyethylene Sheathing Compound for ADSS Optical Cable
-
Eco-Friendly Rodent-Proof and Termite-Proof Nylon Sheathing Compound
-
Flame-Retardant Polyethylene Compound
-
Elastomer Cable Compound
-
Special Cable Compounds and Solutions
Product Performance
KPG-0808 is an optical cable skeleton material developed through special formula by taking imported polyethylene resin as raw material. It has high size stability, smooth surface effect, low shrinkage performance and mechanical property.
Product Model
|
Type |
Product |
Application |
|
KPG-0808 |
Optical Cable Skeleton Material |
Used for the slotted core cable |
Processing technology
The following temperature profile for the extruder is recommended:
|
Zone |
Zone1 |
Zone2 |
Zone3 |
Zone4 |
Zone5 |
Head |
Die |
|
Temperature℃ |
165 |
165 |
170 |
170 |
170 |
170 |
170 |
Storage and Transportation
KPG-0808 is hygroscopic. It should be stored in dry and ventilated warehouse. And drying treatment is required after long-term storage. Drying temperature is 75℃. Drying time is 3 hours. Storage period should be less than 12 months.
Performance metrics
|
NO. |
Item |
Unit |
Typical |
Test method |
|
1 |
Melting Index |
g/10min |
0.3 |
GB/T 2951.41 |
|
2 |
Density |
g/cm³ |
0.952 |
GB/T 1033 |
|
3 |
Tensile Strength |
MPa |
28 |
GB/T 1040 |
|
4 |
Yield strength |
MPa |
26 |
GB/T 1040 |
|
5 |
Elongation at Break |
% |
800 |
GB/T 1040 |
|
6 |
Low temperature elongation at break |
% |
487 |
GB/T 2951.13 |
|
7 |
Brittle temperature（-76℃） |
pcs |
0/10 |
GB/T 5470 |
|
8 |
ESCR |
h |
> 1000 |
GB/T 2951.41 |
|
9 |
OIT 200℃ |
min |
45 |
GB/T 2951.39 |
|
10 |
Dielectric Strength |
MV/mm |
28 |
GB/T 1408 |
|
11 |
Volume Resistivity at 20℃ |
Ω·m |
4.5 × 1014 |
GB/T 1410 |
|
12 |
Dielectric constant |
— |
2.1 |
GB/T 1409 |
|
13 |
Dielectric loss tangent |
|
0.0003 |
GB/T 1409 |
Keywords:
Special Cable Compounds and Solutions
Production strength
Honorary Qualifications
Related products
Contact Information
Company office
Sales Hotline
Procurement Hotline
Company headquarters
No. 168, Yanjiang Road, Xiaochi Town, Huangmei County, Hubei Province
Follow us