Hubei Kepuda Polymer Material Co., Ltd.
Irradiation Crosslinkable Low-Smoke Halogen-Free Flame-retardant Polyolefin Cable Compound
Category:
Irradiation crosslinkable, low-smoke halogen-free flame-retardant polyolefin cable compound, based on special POE resin, is produced by special technology with adding modifier, flame-retardant and other special additives.
Contact:
Product Center
-
Polyethylene Compound
-
Thermoplastic Low-Smoke Halogen-Free Flame-Retardant Polyolefin Cable Compound
-
Irradiation Crosslinkable Low-Smoke Halogen-Free Flame-retardant Polyolefin Cable Compound
-
Anti-Tracking Polyethylene Sheathing Compound for ADSS Optical Cable
-
Eco-Friendly Rodent-Proof and Termite-Proof Nylon Sheathing Compound
-
Flame-Retardant Polyethylene Compound
-
Elastomer Cable Compound
-
Special Cable Compounds and Solutions
Product Performance
Irradiation crosslinkable, low-smoke halogen-free flame-retardant polyolefin cable compound, based on special POE resin, is produced by special technology with adding modifier, flame-retardant and other special additives.
Product Model
| Type | Product | Application |
| KPF-5105 |
105℃ irradiation crosslinkable, low-smoke halogen-free flame-retardant polyolefin cable compound |
For wire and car wire |
| KPF-5125 |
125℃ irradiation crosslinkable, low-smoke halogen-free flame-retardant polyolefin cable compound |
For wire and car wire |
| KPF-5125NY |
125℃ irradiation crosslinkable, low-smoke, halogen-free, flame-retardant and oil resistant polyolefin cable compound |
For wire and car wire |
| KPF-5150 |
150℃irradiation crosslinkable, low-smoke halogen-free flame-retardant polyolefin cable compound |
For wire and car wire |
Processing technology
The following temperature profile for the extruder is recommended:
|
Zone |
Zone1 |
Zone2 |
Zone3 |
Zone4 |
Zone5 |
Head |
Die |
|
|
Temperature ℃ |
KPF-5105 KPF-5125 |
120 | 130 | 140 | 150 | 155 | 160 | 160 |
|
KPF-5125NY KPF-5150 |
110 | 120 | 135 | 140 | 145 | 150 | 150 | |
Storage and Transportation
Product adopts moisture proof packaging; net weight is 25kg; be stored in clean, dry and ventilated place; drying treatment is required after long-term storage; drying temperature is 75℃; drying time is 3 hours; storage period should be less than 12 months.
Performance metrics
|
Item |
Unit |
Typical value |
||||
|
KPF-5105 |
KPF-5125 |
KPF-5125NY |
KPF-5150 |
|||
|
Density |
g/cm3 |
1.45 |
1.46 |
1.46 |
1.48 |
|
|
Service temperature |
℃ |
105 |
125 |
125 |
150 |
|
|
Tensile strength at break |
MPa |
12.5 |
12.3 |
13.2 |
12.2 |
|
|
Elongation at break |
% |
190 |
195 |
220 |
200 |
|
|
（200℃，15min，0.2MPa） |
Elongation under load |
% |
56 |
58 |
62 |
40 |
|
Permanent deformation after cooling |
% |
3 |
5 |
3 |
2 |
|
|
Air oven-7days（168hrs.） At 158℃ |
Variation on Tensile Strength |
% |
-6* |
-13 |
-6 |
9▲ |
|
Variation on Elongation |
% |
-8* |
-9 |
-9 |
-11▲ |
|
|
OI |
% |
35 |
36 |
35 |
36 |
|
|
Smoke Density |
Non-flame |
% |
185 |
184 |
174 |
150 |
|
Flame |
% |
65 |
70 |
70 |
60 |
|
|
Acid gas contained |
mg/g |
0.03 |
0.02 |
0.01 |
0.01 |
|
|
pH Value |
- |
5.6 |
5.7 |
5.6 |
5.8 |
|
|
Electrical Conductivity |
μS/mm |
1.7 |
1.9 |
1.6 |
2.1 |
|
|
Toxicity index |
- |
1.4 |
1.5 |
1.3 |
1.4 |
|
|
902# Oil resistant |
Retention of tensile strength |
% |
- |
- |
82 |
- |
|
Retention of elongation |
% |
- |
- |
80 |
- |
|
Note: Aging conditions marked with * are 136°C for 168 hours; those marked with ▲ are 180°C for 168 hours.
Keywords:
Irradiation Crosslinkable Low-Smoke Halogen-Free Flame-retardant Polyolefin Cable Compound
Production strength
Honorary Qualifications
Related products
Contact Information
Company office
Sales Hotline
Procurement Hotline
Company headquarters
No. 168, Yanjiang Road, Xiaochi Town, Huangmei County, Hubei Province
Follow us